Process:
ALL SURFACES SHALL BE SOLVENT WIPED IN ACCORDANCE WITH SSPC-SP1, AND SHALL BE PREPARED BY ABRASIVE BLASTING TO NEAR-WHITE METAL(NACE NO. 2/SSPC-SP-10) TO 2 TO 4 MIL SURFACE PROFILE. HOT COAT PRIME USING TIGER DRYLAC ZINC RICH PRIMER 69/90350 OR EQUAL TO 3 MIL THICKNESS. TOP-COAT WITH SHERWIN- WILLIAMS EAS8-30034(MIL-PRF-23236, TYPE VIII CLASS 7, GRADE D) OR EQUAL TO 3 MIL THICKNESS. FINAL DESPOSITION OF LOW OR HIGH COATING THICKNESS SHALL BE AS IN SSPC-PA-2. FINAL TOTAL MIL THICKNESS TARGET IS 6 MIL.